摘要: |
通过粘接面处理、粘接压力、胶层厚度、胶层涂刷方式等方面对三元乙丙橡胶粘接性能进行了研究。结果表明,铝合金应喷砂后阳极化、三元乙丙橡胶生胶用乙酸乙脂擦拭、熟胶进行表面打磨;采用三次刷涂,胶层厚度控制在0.1~0.15mm;硫化压力5~10MPa是较好的粘接工艺方法。 |
关键词: 三元乙丙橡胶;粘接工艺;粘接性能 |
基金项目: |
|
Study on Bonding Process of EPDM |
Li Hui1, Deng Defeng2
|
1.The Second Artillery Military Representative of Jianghe Chemical Plant, Xiaogan 432000;2. Jiangbei Machinery Engineering Co., Ltd., Xiaogan 432000
|
Abstract: |
Bonding properties of EPDM are researched through treating methods on bonding surface, bonding pressure, layer thickness and coating method in this article. Results show that anodizing after aluminium alloy sand-blasting, cleaning EPDM raw rubber with ethyl acetate, polishing EPDM cured rubber surface, coating three times, keeping layer thickness between 0.1~0.15mm and being sulfurized at 5~10MPa are better for bonding process of EPDM. |
Key words: EPDM;bonding process;bonding property |