摘要: |
针对钨渗铜材料在烧结成型、熔渗等过程中可能出现的孔洞、夹杂、渗铜不均等缺陷,采用水浸超声波检测方法对其进行内部质量检测,并分析检测结果;在此基础之上,将部分典型缺陷C扫描检测结果同射线检测结果进行对比,从而验证水浸超声检测方法的可行性与适用性,达到快速、便捷检测的目的。同时,水浸超声检测方法还能够实现对缺陷位置和尺寸的定量,为后续强度分析、寿命预测提供数据参考。 |
关键词: 钨渗铜;水浸超声检测;C扫描图像;射线检测;缺陷定量 |
基金项目: |
|
Water-immersion Ultrasonic Testing of Copper Infiltrated Tungsten Material Used in Aerospace |
Kang Da Zhang Hong Ma Zhaoguang Li Shiqi Lin Shanshan
|
Beijing Power Machinery Institute, Beijing 100074
|
Abstract: |
To solve the problems of defect, holes, and inclusions in the process of sintering forming and melting infiltration of copper-tungsten materials, the water-immersion ultrasonic testing method was used to conduct internal quality inspection. Based on the results, the comparison was made between ultrasonic C scan result and X-ray results to verify the reliability and feasibility of water-immersion ultrasonic testing method. Meanwhile, the water-immersion ultrasonic testing method can provide quantitative results of location and size, so as to provide data reference for subsequent strength analysis and life prediction. |
Key words: Beijing Power Machinery Institute, Beijing 100074 |