摘要: |
针对TC18钛合金进行闪光焊工艺试验,分析研究了该合金闪光焊接头的组织与性能。结果表明:可以采用闪光焊焊接TC18钛合金,焊后不进行热处理,其接头强度、延伸率和冲击韧性均比较低,分别为母材的87.1%、68.5%和15.1%,若焊后进行热处理,接头强度与相同热处理状态的母材等强,延伸率和冲击韧性分别达到母材的52.7%和35.5%。 |
关键词: TC18钛合金;闪光焊;组织;性能 |
基金项目: |
|
Microstructure and Properties of Flash Welding Joints ofTC18 Titanium Alloy |
Wang Jinxue1, Yuan Hong1, Yu Huai1, Zhang Guodong1, Xiao Zhixiang2, Jiang Feilong2, Liu Zhong2
|
1. Beijing Institution of Aeronautical Materials, Beijing 100095;2. Guiyang Anda Aerospace Material Engineering Co., Ltd., Guiyang 550009
|
Abstract: |
Flash Welding experiments of TC18 Titanium Alloy were proceeded, then the microstructure and properties of Flash Welding joints of this alloy were studied.The results show that TC18 Titanium Alloy can be welded by the method of Flash Welding.The strength, elongation and impact toughness of the welding joints were respectively 87.1%, 68.5% and 15.1% of the basic metal, which have a low level without heat treatment after welding. If the heat treatment were proceeded after welding, the shrength of the joints was as the same as the basic metal, the elongation and impact toughness were respectively 52.7% and 35.5% of the basic metal. |
Key words: TC18 Titanium Alloy;Flash Welding;microstructure;properties |